Deep learning method for analysis and segmentation of fatigue damage in X-ray computed tomography data for fiber-reinforced polymers
出版年份 2022 全文链接
标题
Deep learning method for analysis and segmentation of fatigue damage in X-ray computed tomography data for fiber-reinforced polymers
作者
关键词
-
出版物
COMPOSITES SCIENCE AND TECHNOLOGY
Volume 230, Issue -, Pages 109781
出版商
Elsevier BV
发表日期
2022-10-12
DOI
10.1016/j.compscitech.2022.109781
参考文献
相关参考文献
注意:仅列出部分参考文献,下载原文获取全部文献信息。- Road surface detection and differentiation considering surface damages
- (2021) Thiago Rateke et al. AUTONOMOUS ROBOTS
- Layup Design Optimization for E-glass Woven Roving Fabric Reinforced Polyester Composite Laminates Produced by VARTM
- (2021) Raif Sakin FIBERS AND POLYMERS
- Quantifying effects of manufacturing methods on fiber orientation in unidirectional composites using structure tensor analysis
- (2021) N. Jeppesen et al. COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING
- High temperature fatigue of carbon/polyimide 8-harness satin woven composites. Part I: Digital Image Correlation and Micro-Computed Tomography damage characterization
- (2020) Yannick Pannier et al. COMPOSITE STRUCTURES
- Study on the fractal dimension and evolution of matrix crack in cross-ply GFRP laminates
- (2020) Wen Jiang et al. THEORETICAL AND APPLIED FRACTURE MECHANICS
- Damage evolution of 3D woven carbon/epoxy composites under tension-tension fatigue loading based on synchrotron radiation computed tomography (SRCT)
- (2020) Licheng Guo et al. INTERNATIONAL JOURNAL OF FATIGUE
- Fatigue life and damage evolution in woven GFRP angle ply laminates
- (2020) Kalyan Kumar Singh et al. INTERNATIONAL JOURNAL OF FATIGUE
- Experimental and Analytical Study on Residual Stiffness/Strength of CFRP Tendons under Cyclic Loading
- (2020) Chao Wang et al. Materials
- The fatigue of carbon fibre reinforced plastics - A review
- (2019) Parvez Alam et al. COMPOSITES PART B-ENGINEERING
- Stiffness degradation of composite laminates due to matrix cracking and induced delamination during tension-tension fatigue
- (2019) Hamed Pakdel et al. ENGINEERING FRACTURE MECHANICS
- Fatigue damage evolution in thick composite laminates: Combination of X-ray tomography, acoustic emission and digital image correlation
- (2019) Abderrahmane Djabali et al. COMPOSITES SCIENCE AND TECHNOLOGY
- Development of an energy-based approach for optimized frequency selection for fatigue testing on polymers – Exemplified on polyamide 6
- (2019) Daniel Hülsbusch et al. POLYMER TESTING
- In situ experimental investigation on the out-plane damage evolution of 3D woven carbon-fiber reinforced composites
- (2018) Zhixing Li et al. COMPOSITES SCIENCE AND TECHNOLOGY
- Computed tomography informed composite damage state model generation
- (2018) Andrew Ellison et al. JOURNAL OF COMPOSITE MATERIALS
- Porous Structure Reconstruction Using Convolutional Neural Networks
- (2018) Yuzhu Wang et al. Mathematical Geosciences
- A study of induced delamination and failure in woven composite laminates subject to short-beam shear testing
- (2018) J.J. Espadas-Escalante et al. ENGINEERING FRACTURE MECHANICS
- Fatigue life prediction of composite structures based on online stiffness monitoring
- (2017) Junda Zong et al. JOURNAL OF REINFORCED PLASTICS AND COMPOSITES
- Evolution of damage during the fatigue of 3D woven glass-fibre reinforced composites subjected to tension–tension loading observed by time-lapse X-ray tomography
- (2016) B. Yu et al. COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING
- Visual Analysis of Defects in Glass Fiber Reinforced Polymers for 4DCT InterruptedIn situTests
- (2016) Alexander Amirkhanov et al. COMPUTER GRAPHICS FORUM
- Quantitative analysis of fatigue cracks in laminated carbon fibre-reinforced polymer composites using micro-computed tomography
- (2015) Naglaa ElAgamy et al. JOURNAL OF COMPOSITE MATERIALS
- Fatigue and post-fatigue stress–strain analysis of a 5-harness satin weave carbon fibre reinforced composite
- (2012) S. Daggumati et al. COMPOSITES SCIENCE AND TECHNOLOGY
- Damage Assessment of CFRP [90/±45/0] Composite Laminates over Fatigue Cycles
- (2011) G. R. Ahmadzadeh et al. APPLIED COMPOSITE MATERIALS
- In situ fibre fracture measurement in carbon–epoxy laminates using high resolution computed tomography
- (2011) A.E. Scott et al. COMPOSITES SCIENCE AND TECHNOLOGY
- Residual Stiffness of Cracked Cross-Ply Composite Laminates Under Multi-Axial In-plane Loading
- (2010) Costas Soutis et al. APPLIED COMPOSITE MATERIALS
- Local damage in a 5-harness satin weave composite under static tension: Part I – Experimental analysis
- (2010) S. Daggumati et al. COMPOSITES SCIENCE AND TECHNOLOGY
- Segmentation of X-ray computed tomography images of porous materials: A crucial step for characterization and quantitative analysis of pore structures
- (2009) Pavel Iassonov et al. WATER RESOURCES RESEARCH
Find Funding. Review Successful Grants.
Explore over 25,000 new funding opportunities and over 6,000,000 successful grants.
ExploreAsk a Question. Answer a Question.
Quickly pose questions to the entire community. Debate answers and get clarity on the most important issues facing researchers.
Get Started