Comparison of calcium–magnesium-alumina-silicate (CMAS) resistance behavior of produced with electron beam physical vapor deposition (EB-PVD) method YSZ and Gd2Zr2O7/YSZ thermal barrier coatings systems
出版年份 2021 全文链接
标题
Comparison of calcium–magnesium-alumina-silicate (CMAS) resistance behavior of produced with electron beam physical vapor deposition (EB-PVD) method YSZ and Gd2Zr2O7/YSZ thermal barrier coatings systems
作者
关键词
Molten silicate interaction, Cold gas dynamic spray (CGDS), Electron-beam physical vapor deposition (EB-PVD), CoNiCrAlY, Gadolinium zirconate (GZO), Yttria-stabilized zirconia (YSZ)
出版物
VACUUM
Volume 194, Issue -, Pages 110576
出版商
Elsevier BV
发表日期
2021-09-02
DOI
10.1016/j.vacuum.2021.110576
参考文献
相关参考文献
注意:仅列出部分参考文献,下载原文获取全部文献信息。- Oxidation and hot corrosion resistance of HVOF/EB-PVD thermal barrier coating system
- (2021) Kadir Mert Doleker et al. SURFACE & COATINGS TECHNOLOGY
- Performance of single YSZ, Gd2Zr2O7 and double-layered YSZ/Gd2Zr2O7 thermal barrier coatings in isothermal oxidation test conditions
- (2020) Kadir Mert Doleker et al. VACUUM
- Cyclic Hot Corrosion Failure Behaviors of EB-PVD TBC Systems in the Presence of Sulfate and Vanadate Molten Salts
- (2019) Yasin Ozgurluk et al. Coatings
- Hot corrosion behavior of YSZ, Gd 2 Zr 2 O 7 and YSZ/Gd 2 Zr 2 O 7 thermal barrier coatings exposed to molten sulfate and vanadate salt
- (2018) Yasin Ozgurluk et al. APPLIED SURFACE SCIENCE
- Calcium-magnesium-alumino-silicate induced degradation and failure of La 2 (Zr 0.7 Ce 0.3 ) 2 O 7 /YSZ double-ceramic–layer thermal barrier coatings prepared by electron beam-physical vapor deposition
- (2018) Xin Zhou et al. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
- Isothermal oxidation and thermal cyclic behaviors of YSZ and double-layered YSZ/La 2 Zr 2 O 7 thermal barrier coatings (TBCs)
- (2018) Kadir Mert Doleker et al. SURFACE & COATINGS TECHNOLOGY
- Evaluation of oxidation and thermal cyclic behavior of YSZ, Gd2Zr2O7 and YSZ/Gd2Zr2O7 TBCs
- (2018) Kadir Mert Doleker et al. SURFACE & COATINGS TECHNOLOGY
- The Microstructural Investigation of Vermiculite-Infiltrated Electron Beam Physical Vapor Deposition Thermal Barrier Coatings
- (2018) Yasin Ozgurluk et al. Open Chemistry
- Microstructural characterization of GZ/CYSZ thermal barrier coatings after thermal shock and CMAS+hot corrosion test
- (2017) Mustafa Guven Gok et al. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
- Comparison of oxidation behavior of YSZ and Gd 2 Zr 2 O 7 thermal barrier coatings (TBCs)
- (2017) Kadir Mert Doleker et al. SURFACE & COATINGS TECHNOLOGY
- Effect of high vacuum heat treatment on microstructure and cyclic oxidation resistance of HVOF-CoNiCrAlY coatings
- (2017) D. Salehi Doolabi et al. VACUUM
- Effect of shot peening on the oxidation behavior of thermal barrier coatings
- (2015) Abdullah Cahit Karaoglanli et al. APPLIED SURFACE SCIENCE
- Calcium–magnesium–aluminosilicate corrosion behaviors of rare-earth disilicates at 1400°C
- (2013) Jia Liu et al. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
- Preparation and thermophysical properties of fluorite-type samarium–dysprosium–cerium oxides
- (2013) Zhang Hongsong et al. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
- Degradation of La2Zr2O7 and other novel EB-PVD thermal barrier coatings by CMAS (CaO–MgO–Al2O3–SiO2) and volcanic ash deposits
- (2013) Uwe Schulz et al. SURFACE & COATINGS TECHNOLOGY
- Environmental degradation of thermal-barrier coatings by molten deposits
- (2012) Carlos G. Levi et al. MRS BULLETIN
- Degradation of EB-PVD thermal barrier coatings caused by CMAS deposits
- (2012) Hui Peng et al. Progress in Natural Science-Materials International
- Plasma sprayed gadolinium zirconate thermal barrier coatings that are resistant to damage by molten Ca–Mg–Al–silicate glass
- (2012) Julie M. Drexler et al. SURFACE & COATINGS TECHNOLOGY
- Calcium–magnesium–alumino-silicate (CMAS) degradation of EB-PVD thermal barrier coatings: Characterization of CMAS damage on ex-service high pressure blade TBCs
- (2012) M.H. Vidal-Setif et al. SURFACE & COATINGS TECHNOLOGY
- Structure and durability evaluation of YSZ+Al2O3 composite TBCs with APS and HVOF bond coats under thermal cycling conditions
- (2011) A.C. Karaoglanli et al. SURFACE & COATINGS TECHNOLOGY
- High-Temperature Corrosion of EB-PVD Yttria Partially Stabilized Zirconia Thermal Barrier Coatings with an Artificial Volcanic Ash Overlay
- (2010) Peter Mechnich et al. JOURNAL OF THE AMERICAN CERAMIC SOCIETY
- Investigating the microstructure and composition of cold gas-dynamic spray (CGDS) Ti powder deposited on Al 6063 substrate
- (2010) Charles K.S. Moy et al. SURFACE & COATINGS TECHNOLOGY
- Oxidation behaviour of CoNiCrAlY bond coats produced by plasma, HVOF and cold gas dynamic spraying
- (2010) P. Richer et al. SURFACE & COATINGS TECHNOLOGY
- Infiltration-Inhibiting Reaction of Gadolinium Zirconate Thermal Barrier Coatings with CMAS Melts
- (2008) Stephan Krämer et al. JOURNAL OF THE AMERICAN CERAMIC SOCIETY
- Mechanisms of cracking and delamination within thick thermal barrier systems in aero-engines subject to calcium-magnesium-alumino-silicate (CMAS) penetration
- (2008) S. Krämer et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- CoNiCrAlY microstructural changes induced during Cold Gas Dynamic Spraying
- (2008) P. Richer et al. SURFACE & COATINGS TECHNOLOGY
- The effect of pre-oxidation atmosphere on the durability of EB-PVD thermal barrier coatings with CoNiCrAlY bond coats
- (2007) Mineaki Matsumoto et al. SURFACE & COATINGS TECHNOLOGY
Publish scientific posters with Peeref
Peeref publishes scientific posters from all research disciplines. Our Diamond Open Access policy means free access to content and no publication fees for authors.
Learn MoreBecome a Peeref-certified reviewer
The Peeref Institute provides free reviewer training that teaches the core competencies of the academic peer review process.
Get Started