Comparison of calcium–magnesium-alumina-silicate (CMAS) resistance behavior of produced with electron beam physical vapor deposition (EB-PVD) method YSZ and Gd2Zr2O7/YSZ thermal barrier coatings systems
Published 2021 View Full Article
- Home
- Publications
- Publication Search
- Publication Details
Title
Comparison of calcium–magnesium-alumina-silicate (CMAS) resistance behavior of produced with electron beam physical vapor deposition (EB-PVD) method YSZ and Gd2Zr2O7/YSZ thermal barrier coatings systems
Authors
Keywords
Molten silicate interaction, Cold gas dynamic spray (CGDS), Electron-beam physical vapor deposition (EB-PVD), CoNiCrAlY, Gadolinium zirconate (GZO), Yttria-stabilized zirconia (YSZ)
Journal
VACUUM
Volume 194, Issue -, Pages 110576
Publisher
Elsevier BV
Online
2021-09-02
DOI
10.1016/j.vacuum.2021.110576
References
Ask authors/readers for more resources
Related references
Note: Only part of the references are listed.- Oxidation and hot corrosion resistance of HVOF/EB-PVD thermal barrier coating system
- (2021) Kadir Mert Doleker et al. SURFACE & COATINGS TECHNOLOGY
- Performance of single YSZ, Gd2Zr2O7 and double-layered YSZ/Gd2Zr2O7 thermal barrier coatings in isothermal oxidation test conditions
- (2020) Kadir Mert Doleker et al. VACUUM
- Cyclic Hot Corrosion Failure Behaviors of EB-PVD TBC Systems in the Presence of Sulfate and Vanadate Molten Salts
- (2019) Yasin Ozgurluk et al. Coatings
- Hot corrosion behavior of YSZ, Gd 2 Zr 2 O 7 and YSZ/Gd 2 Zr 2 O 7 thermal barrier coatings exposed to molten sulfate and vanadate salt
- (2018) Yasin Ozgurluk et al. APPLIED SURFACE SCIENCE
- Calcium-magnesium-alumino-silicate induced degradation and failure of La 2 (Zr 0.7 Ce 0.3 ) 2 O 7 /YSZ double-ceramic–layer thermal barrier coatings prepared by electron beam-physical vapor deposition
- (2018) Xin Zhou et al. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
- Isothermal oxidation and thermal cyclic behaviors of YSZ and double-layered YSZ/La 2 Zr 2 O 7 thermal barrier coatings (TBCs)
- (2018) Kadir Mert Doleker et al. SURFACE & COATINGS TECHNOLOGY
- Evaluation of oxidation and thermal cyclic behavior of YSZ, Gd2Zr2O7 and YSZ/Gd2Zr2O7 TBCs
- (2018) Kadir Mert Doleker et al. SURFACE & COATINGS TECHNOLOGY
- The Microstructural Investigation of Vermiculite-Infiltrated Electron Beam Physical Vapor Deposition Thermal Barrier Coatings
- (2018) Yasin Ozgurluk et al. Open Chemistry
- Microstructural characterization of GZ/CYSZ thermal barrier coatings after thermal shock and CMAS+hot corrosion test
- (2017) Mustafa Guven Gok et al. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
- Comparison of oxidation behavior of YSZ and Gd 2 Zr 2 O 7 thermal barrier coatings (TBCs)
- (2017) Kadir Mert Doleker et al. SURFACE & COATINGS TECHNOLOGY
- Effect of high vacuum heat treatment on microstructure and cyclic oxidation resistance of HVOF-CoNiCrAlY coatings
- (2017) D. Salehi Doolabi et al. VACUUM
- Effect of shot peening on the oxidation behavior of thermal barrier coatings
- (2015) Abdullah Cahit Karaoglanli et al. APPLIED SURFACE SCIENCE
- Calcium–magnesium–aluminosilicate corrosion behaviors of rare-earth disilicates at 1400°C
- (2013) Jia Liu et al. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
- Preparation and thermophysical properties of fluorite-type samarium–dysprosium–cerium oxides
- (2013) Zhang Hongsong et al. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
- Degradation of La2Zr2O7 and other novel EB-PVD thermal barrier coatings by CMAS (CaO–MgO–Al2O3–SiO2) and volcanic ash deposits
- (2013) Uwe Schulz et al. SURFACE & COATINGS TECHNOLOGY
- Environmental degradation of thermal-barrier coatings by molten deposits
- (2012) Carlos G. Levi et al. MRS BULLETIN
- Degradation of EB-PVD thermal barrier coatings caused by CMAS deposits
- (2012) Hui Peng et al. Progress in Natural Science-Materials International
- Plasma sprayed gadolinium zirconate thermal barrier coatings that are resistant to damage by molten Ca–Mg–Al–silicate glass
- (2012) Julie M. Drexler et al. SURFACE & COATINGS TECHNOLOGY
- Calcium–magnesium–alumino-silicate (CMAS) degradation of EB-PVD thermal barrier coatings: Characterization of CMAS damage on ex-service high pressure blade TBCs
- (2012) M.H. Vidal-Setif et al. SURFACE & COATINGS TECHNOLOGY
- Structure and durability evaluation of YSZ+Al2O3 composite TBCs with APS and HVOF bond coats under thermal cycling conditions
- (2011) A.C. Karaoglanli et al. SURFACE & COATINGS TECHNOLOGY
- High-Temperature Corrosion of EB-PVD Yttria Partially Stabilized Zirconia Thermal Barrier Coatings with an Artificial Volcanic Ash Overlay
- (2010) Peter Mechnich et al. JOURNAL OF THE AMERICAN CERAMIC SOCIETY
- Investigating the microstructure and composition of cold gas-dynamic spray (CGDS) Ti powder deposited on Al 6063 substrate
- (2010) Charles K.S. Moy et al. SURFACE & COATINGS TECHNOLOGY
- Oxidation behaviour of CoNiCrAlY bond coats produced by plasma, HVOF and cold gas dynamic spraying
- (2010) P. Richer et al. SURFACE & COATINGS TECHNOLOGY
- Infiltration-Inhibiting Reaction of Gadolinium Zirconate Thermal Barrier Coatings with CMAS Melts
- (2008) Stephan Krämer et al. JOURNAL OF THE AMERICAN CERAMIC SOCIETY
- Mechanisms of cracking and delamination within thick thermal barrier systems in aero-engines subject to calcium-magnesium-alumino-silicate (CMAS) penetration
- (2008) S. Krämer et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- CoNiCrAlY microstructural changes induced during Cold Gas Dynamic Spraying
- (2008) P. Richer et al. SURFACE & COATINGS TECHNOLOGY
- The effect of pre-oxidation atmosphere on the durability of EB-PVD thermal barrier coatings with CoNiCrAlY bond coats
- (2007) Mineaki Matsumoto et al. SURFACE & COATINGS TECHNOLOGY
Find the ideal target journal for your manuscript
Explore over 38,000 international journals covering a vast array of academic fields.
SearchAdd your recorded webinar
Do you already have a recorded webinar? Grow your audience and get more views by easily listing your recording on Peeref.
Upload Now