出版年份 2018 全文链接
标题
Crack growth rates and microstructure feature of initiation region for very-high-cycle fatigue of a high-strength steel
作者
关键词
-
出版物
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
Volume 41, Issue 8, Pages 1717-1732
出版商
Wiley
发表日期
2018-04-02
DOI
10.1111/ffe.12811
参考文献
相关参考文献
注意:仅列出部分参考文献,下载原文获取全部文献信息。- Microscopic damage evolution during very-high-cycle fatigue (VHCF) of tempered martensitic steel
- (2017) U. Krupp et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- Fatigue crack closure: a review of the physical phenomena
- (2017) R. Pippan et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- Effects of inclusions on the very high cycle fatigue behaviour of steels
- (2017) André Pineau et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- Reason for the transition of fatigue crack initiation site from surface to subsurface inclusions in high-strength steels
- (2017) P. Grad et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- The nature and the mechanism of crack initiation and early growth for very-high-cycle fatigue of metallic materials – An overview
- (2017) Youshi Hong et al. THEORETICAL AND APPLIED FRACTURE MECHANICS
- Analysis of microdamage in a nickel-base alloy during very high cycle fatigue
- (2016) Guocai Chai FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- Effects of specimen size on fatigue life of metallic materials in high-cycle and very-high-cycle fatigue regimes
- (2016) C. Sun et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- Nanograin layer formation at crack initiation region for very-high-cycle fatigue of a Ti-6Al-4V alloy
- (2016) H. Su et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- Faceted crack initiation characteristics for high-cycle and very-high-cycle fatigue of a titanium alloy under different stress ratios
- (2016) Xiaolong Liu et al. INTERNATIONAL JOURNAL OF FATIGUE
- The formation mechanism of characteristic region at crack initiation for very-high-cycle fatigue of high-strength steels
- (2016) Youshi Hong et al. INTERNATIONAL JOURNAL OF FATIGUE
- Very-high-cycle fatigue behavior of a structural steel with and without induced surface defects
- (2016) Qingqing Jiang et al. INTERNATIONAL JOURNAL OF FATIGUE
- Recent developments in ultrasonic fatigue
- (2015) H. Mayer FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- Microscopic and nanoscopic observations of metallurgical structures around inclusions at interior crack initiation site for a bearing steel in very high-cycle fatigue
- (2015) T. Sakai et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- Mechanisms and modeling of subsurface fatigue cracking in metals
- (2013) A.A. Shanyavskiy ENGINEERING FRACTURE MECHANICS
- A fracture mechanics approach to interior fatigue crack growth in the very high cycle regime
- (2013) Takeshi Ogawa et al. ENGINEERING FRACTURE MECHANICS
- Influence of mean stress and variable amplitude loading on the fatigue behaviour of a high-strength steel in VHCF regime
- (2013) M. Sander et al. INTERNATIONAL JOURNAL OF FATIGUE
- Propensities of crack interior initiation and early growth for very-high-cycle fatigue of high strength steels
- (2013) Youshi Hong et al. INTERNATIONAL JOURNAL OF FATIGUE
- Effects of loading condition on very-high-cycle fatigue behaviour and dominant variable analysis
- (2013) ZhengQiang Lei et al. Science China-Physics Mechanics & Astronomy
- On the use of ultrasonic fatigue testing technique – Variable amplitude loadings and crack growth monitoring
- (2013) T. Müller et al. ULTRASONICS
- Effect of residual stresses on crack behaviour in single edge bending specimens
- (2012) M. FARAHANI et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- Effects of inclusion size and location on very-high-cycle fatigue behavior for high strength steels
- (2012) Zhengqiang Lei et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Mechanism of fatigue crack initiation and propagation in the very high cycle fatigue regime of high-strength steels
- (2012) P. Grad et al. SCRIPTA MATERIALIA
- Effects of strength level and loading frequency on very-high-cycle fatigue behavior for a bearing steel
- (2011) Aiguo Zhao et al. INTERNATIONAL JOURNAL OF FATIGUE
- Prediction of threshold value for FGA formation
- (2011) Aiguo Zhao et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Fatigue Strength and Crack Initiation Mechanism of Very-High-Cycle Fatigue for Low Alloy Steels
- (2011) Youshi Hong et al. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE
- Statistical duplex S–N characteristics of high carbon chromium bearing steel in rotating bending in very high cycle regime
- (2009) T. Sakai et al. INTERNATIONAL JOURNAL OF FATIGUE
Discover Peeref hubs
Discuss science. Find collaborators. Network.
Join a conversationFind the ideal target journal for your manuscript
Explore over 38,000 international journals covering a vast array of academic fields.
Search