JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE
卷 28, 期 7, 页码 4111-4119出版社
SPRINGER
DOI: 10.1007/s11665-019-04162-4
关键词
DSC; hardness; high-entropy alloy; thermal conductivity
资金
- Institute (Malaviya National Institute of Technology, Jaipur)
Al0.4FeCrNiCox (x = 0, 0.25, 0.5, 1.0 mol) high-entropy alloys are developed by arc melting route to investigate the effect of cobalt content on thermal, mechanical, and microstructural properties. The phase, microstructure, and chemical composition are analyzed using x-ray diffraction, transmission electron microscope, and scanning electron microscope with attached energy-dispersive x-ray spectrometer. The obtained results have shown that the Al0.4FeCrNiCox (x = 0-0.5 mol) high-entropy alloys form a simple FCC + BCC-type solid solution and Al0.4FeCrNiCox=1 HEA forms a single-phase FCC structure. The compressive yield strength, microhardness, and thermal conductivity are observed to decrease from 965.22 to 233.37 MPa, 253.6 to 155.6 HV, and from 4.87 to 2.674 W/mK, respectively, whereas the electrical resistivity is observed to increase from 150.30 to 273.74 mu Omega-cm with the addition of cobalt from x = 0-1 mol. Differential scanning calorimetry analysis has indicated that the Al0.4FeCrNiCox (x = 0, 0.25, 0.5, 1.0 mol) high-entropy alloys are thermally stable up to 1000 degrees C.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据