Sulfide Stress Corrosion Cracking Behavior of G105 and S135 High-Strength Drill Pipe Steels in H2S Environment
出版年份 2019 全文链接
标题
Sulfide Stress Corrosion Cracking Behavior of G105 and S135 High-Strength Drill Pipe Steels in H2S Environment
作者
关键词
cleavage fracture, drill pipe steel, hydrogen sulfide, stress corrosion cracking
出版物
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE
Volume 28, Issue 3, Pages 1707-1718
出版商
Springer Nature
发表日期
2019-02-22
DOI
10.1007/s11665-019-03913-7
参考文献
相关参考文献
注意:仅列出部分参考文献,下载原文获取全部文献信息。- Fatigue behavior of high-strength steel S135 under coupling multi-factor in complex environments
- (2018) Dezhi Zeng et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Electrochemical characterization and stress corrosion cracking of E690 high strength steel in wet-dry cyclic marine environments
- (2018) Wenkui Hao et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- A comprehensive analysis on the longitudinal fracture in the tool joints of drill pipes
- (2017) Xinhu Wang et al. ENGINEERING FAILURE ANALYSIS
- Effect of Hydrogen Charging on the Stress Corrosion Behavior of 2205 Duplex Stainless Steel Under 3.5 wt.% NaCl Thin Electrolyte Layer
- (2017) Tianliang Zhao et al. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE
- Effects of H2S/HS− on Stress Corrosion Cracking Behavior of X100 Pipeline Steel Under Simulated Sulfate-Reducing Bacteria Metabolite Conditions
- (2017) Q. Liu et al. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE
- Synergistic effects of corrosion time and stress on corrosion of casing steel in H2 S/CO2 gas wells
- (2017) Zhi Zhang et al. MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION
- Hydrogen embrittlement behavior of high strength rail steels: A comparison between pearlitic and bainitic microstructures
- (2017) Weijun Hui et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Comparative study on the stress corrosion cracking of X70 pipeline steel in simulated shallow and deep sea environments
- (2017) Feilong Sun et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Verification of an Electrochemical Model for Aqueous Corrosion of Mild Steel for H2S Partial Pressures up to 0.1 MPa
- (2017) Saba Navabzadeh Esmaeely et al. CORROSION
- Hydrogen assisted crack initiation and propagation in a nickel-based superalloy
- (2016) Zhenbo Zhang et al. ACTA MATERIALIA
- Stress corrosion cracking of E690 steel as a welded joint in a simulated marine atmosphere containing sulphur dioxide
- (2015) H.C. Ma et al. CORROSION SCIENCE
- Corrosion and metallurgical investigation of two supermartensitic stainless steels for oil and gas environments
- (2014) Thiago J. Mesquita et al. CORROSION SCIENCE
- Electrochemical and Sulfide Stress Corrosion Cracking Behaviors of Tubing Steels in a H2S/CO2 Annular Environment
- (2014) Z. Y. Liu et al. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE
- Evaluation of stress corrosion cracking and hydrogen embrittlement in an API grade steel
- (2013) A.H.S. Bueno et al. ENGINEERING FAILURE ANALYSIS
- Sulfide stress cracking resistance of the welded WDL690D HSLA steel in H2S environment
- (2013) F. Huang et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Effect of hydrogen and low temperature on fatigue crack growth of pipeline steels
- (2012) P. Fassina et al. ENGINEERING FRACTURE MECHANICS
- Multi-scale based stochastic damage evolution
- (2010) Jie Li et al. ENGINEERING FAILURE ANALYSIS
- Near-Neutral pH Stress Corrosion Cracking Susceptibility of Plastically Prestrained X70 Steel Weldment
- (2010) Baotong Lu et al. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE
- Effect of microstructure on the sulphide stress cracking susceptibility of a high strength pipeline steel
- (2008) E. Ramírez et al. CORROSION SCIENCE
Discover Peeref hubs
Discuss science. Find collaborators. Network.
Join a conversationFind the ideal target journal for your manuscript
Explore over 38,000 international journals covering a vast array of academic fields.
Search