Indium doped zinc oxide thin films deposited by ultrasonic spray pyrolysis technique: Effect of the substrate temperature on the physical properties

Indium doped zinc oxide (ZnO:In) thin solid films were deposited on soda-lime glass substrates by the ultrasonic spray pyrolysis technique. The effect of the substrate temperature on the electrical, morphology, and optical characteristics of ZnO:In thin films was studied. It was found that, as the substrate temperature increases, the electrical resistivity decreases, reaching a minimum value in the order of 7.3 x 10(-3) Omega cm, at 415 degrees C. Further increase in the substrate temperature results on an increment on the electrical resistivity of the thin solid films. All the samples were polycrystalline with a well-defined wurtzite structure. The preferred growth shows a switching from a random orientation at low substrates temperatures to (0 0 2) in the case of films deposited at the highest substrate temperature used. As the substrate temperature increases, the corresponding surface morphology changes from an almost faceted pyramidal to round-shaped form. The optical transmittance of the films in a interval of 400 to 700 nm is around 70%, with a band gap value in the order of 3.45 eV. (C) 2011 Elsevier Ltd. All rights reserved.