MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
卷 493, 期 1-2, 页码 251-255出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.msea.2007.05.124
关键词
functionally graded materials; spark plasma sintering; boron carbide; aluminum; nanocomposite
Continuous functionally graded boron carbide aluminum cermets were created using spark plasma sintering. The B4C compacts with large, precipitous density gradients were melt infiltrated with 99.999% Al at 1180 degrees C for 10 min. The microstructure of the material exhibits a gradual change from fully dense B4C with a nominal grain size of 2 pm and a hardness of 32.3 GPa to a B4C-Al cermet with a B4C grain size on the order of 200 nm and a hardness of 8.36 GPa. Prior to melt infiltration, X-ray diffraction data indicates that the B4C compacts have some microstructural defects present. This result is confirmed by the presence of twins on the fully dense fracture surface. Following melt infiltration, X-ray diffraction reveals that some of the defects are dissipated and small amounts of Al3BC are present. (C) 2007 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据