MATERIALS LETTERS
卷 65, 期 1, 页码 104-106出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.matlet.2010.09.028
关键词
Composite materials; Intermetallics; Surface modification; Ball mill; Interface structure; Mechanical properties
资金
- National Natural Science Foundation of China [50901005]
- Beijing Nova Program [2007B016]
A MgLiAl matrix composite reinforced with modified ultrafine YAl2 particles was developed by stirring casting in which YAl2 particles were modified by milling YAl2 and Mg particles The effects of milling on the microstructures of YAl2 particles and the dispersity of YAl2 particles in YAl2-Mg mixture were investigated The microstructures and mechanical properties of the composite were presented The results show that after mix milling elemental magnesium exists around YAl2 particles and YAl2 particles distribute homogeneously in YAl2-Mg mixture YAl2-Mg mix milling is greatly beneficial to control agglomeration of ultrafine YAl2 reinforcement in matrix and the reinforcement is uniformly distributed in the matrix The tensile strength of the 5 vol % YAl(2)p/MgLiAl composite increases by 90% as compared to the matrix alloy while the elongation is keep at 7% Crown Copyright (C) 2010 Published by Elsevier B V All rights reserved
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据