MATERIALS LETTERS
卷 62, 期 14, 页码 2146-2149出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.matlet.2007.11.035
关键词
Al-Si piston alloy; manganese; casting; microstructure; elevated temperature strength
The effects of different amount of trace Mn addition on the elevated temperature tensile strength and microstructure of a low-iron Al-Si piston alloy were investigated by tensile testing, EPMA, SEM and EDX It has been found that with the increase of Mn addition, the elevated temperature tensile strength of the examined alloy exhibits an interesting change: from primary 67.07 Wa, increased to 75.62 MPa and then decreased to 69.67 MPa, 63.72 MPa; finally increased again to 71.92 MPa. Through microstructural analysis, it is found that there occurs an evolution of Mn-bearing intermetallic phases in alloy with the increase of the Mn addition into the alloy. When the amount is 0. 15 wt.%, most of manganese exists in the dendritic Al(9)FeNi phase; ftirther addition of Mn can lead to the formation of plate-like Mn-bearing phases, whose strengthening effect is poor. (C) 2007 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据