Polymer nanocomposite electrolyte; Plasticization; Glass transition temperature; Complex impedance spectroscopy; XRD; Electrical conductivity
资金
- DoE [DE-FG02-01ER45868]
- NASA [NNX08AB12A]
- NASA [NNX08AB12A, 103337] Funding Source: Federal RePORTER
The solid polymer electrolyte films based on polyethylene oxide, NaClO4 with dodecyl amine modified montmorillonite as filler, and polyethylene glycol as plasticizer were prepared by a tape casting method. The effect of plasticization on structural, microstructural, and electrical properties of the materials has been investigated. A systematic change in the structural and microstructural properties of plasticized polymer nanocomposite electrolytes (PPNCEs) on addition of plasticizer was observed in our X-ray diffraction pattern and scanning electron microscopy micrographs. Complex impedance analysis technique was used to calculate the electrical properties of the nanocomposites. Addition of plasticizer has resulted in the lowering of the glass transition temperature, effective dissociation of the salt, and enhancement in the electrical conductivity. The maximum value of conductivity obtained was similar to 4.4 x 10(-6) S cm(-1) (on addition of similar to 20% plasticizer), which is an order of magnitude higher than that of pure polymer nanocomposite electrolyte films (2.82 x 10(-7) S cm(-1)). The enhancement in conductivity on plasticization was well correlated with the change in other physical properties.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据