Silk; Nano-TiO2; Silk mask paper; Formaldehyde; Photocatalytic degradation
资金
- Tianjin Key Laboratory of Pulp and Paper (Tianjin University of Science Technology) [200920]
Silk mask paper with different adsorbability was prepared by changing the beating degree of silk pulp and the basis weight of silk paper, and photocatalytic silk mask paper was prepared by loading nanometer titanium dioxide (nano-TiO2) on the silk mask paper, then degradation of formaldehyde by silk mask paper loading nano-TiO2 under daylight lamps and ultraviolet lamps were investigated, respectively. Results showed that silk mask paper could adsorb formaldehyde and had higher adsorption efficiency in the initial stage, and the adsorption/desorption equilibrium could be basically achieved in 60 minutes. The adsorption capacity of silk mask paper made from silk pulp with beating degree of 45 degrees SR was relatively low, and it increased with the increase of beating degree, but there was little change in adsorption when the beating degree of silk pulp exceeded 65 degrees SR. Under daylight lamps, 26.61 %, 31.42 % and 38.21 % of formaldehyde could be degraded in 180 minutes by silk mask paper loading 1 wt%, 3 wt% and 5 wt% nano-TiO2, respectively. However, under ultraviolet (UV) lamps, 46.23 %, 55.47 % and 66.38 % of formaldehyde could be degraded within the same time, respectively. More formaldehyde could be degraded by photocatalytic silk mask paper under UV lamps than under daylight lamps, and the more the load of nano-TiO2 on the silk mask paper, the higher the degradation rate of formaldehyde within the same time.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据