JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
卷 35, 期 13, 页码 3467-3474出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.jeurceramsoc.2015.06.007
关键词
PZT; 3-1 Type; Self-organization method; Dielectric properties; Piezoelectric properties
资金
- National Natural Science Foundation of China [51172214, 51272301]
- Scientific and Technological Innovation Programs of Higher Education Institutions in Shanxi
- Shanxi Province Science Foundation for Youths [2013021013-6]
In this work, 3-1 type PZT ceramics with unidirectionally aligned channels have been fabricated by ionotropic gelation process of alginate/PZT suspensions. The 3-1 type PZT ceramics with porosity ranging from 36.9% to 60.6% were fabricated by adjusting the initial solid loading (5-25 wt%) of slurries. By incorporating CaO into PZT matrix during the process, the relative permittivity of porous ceramics was reduced, which was beneficial for enhancing the value of hydrostatic figure of merit (HFOM). With regard to the piezoelectric and mechanical properties, due to the combination of highly ordered capillary structure and doping of CaO, 3-1 type PZT ceramics demonstrated excellent performances. As a result, the prepared samples possessed a maximal HFOM value of 7.6 x 10(-12) Pa-1 and compressive strength of 125 MPa. The acoustic impedance (Z) of specimens decreased linearly with increasing porosity, making them promising candidates for application to underwater sonar or medical imaging. (C) 2015 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据