Glass free, non-aqueous LTCC tapes of Bi4(SiO4)3 with high solid loading

Glass free Ei(4)(SiO4)(3) ceramic tapes were prepared by non-aqueous solvent based tape casting technique. A higher powder loading above 65 wt.% was achieved in a silicate system through a judicious selection of suitable dispersants and binder. The amount of dispersant was optimized at 1.0 wt.% based on viscosity and sedimentation analysis. The surface morphology and mechanical strength of the green tapes were investigated. The as-prepared green tape of thickness 70 mu m has an average surface roughness of 320 nm and a tensile strength of 0.37 MPa. The microwave dielectric properties of the green tape (epsilon(r) = 6.2 and tan delta = 0.0390) and sintered tape (epsilon(r) = 13.3 and tan delta = 0.0007) were measured at 15 GHz by using SPDR technique. (C) 2015 Elsevier Ltd. All rights reserved.