期刊
JOURNAL OF THE ELECTROCHEMICAL SOCIETY
卷 163, 期 2, 页码 A13-A18出版社
ELECTROCHEMICAL SOC INC
DOI: 10.1149/2.0011602jes
关键词
-
资金
- NSERC
- 3 M Canada, Co. under Industrial Research Chair program
- Canada Foundation for Innovation
- Atlantic Innovation Fund
- Killam Trusts
NixSi1-x (0 <= x <= 0.5, Delta x = 0.05) alloys were prepared by ball milling and studied as anode materials for lithium ion batteries. Nanocrystalline Si/NiSi2 phases were formed for x <= 0.25. The NiSi phase was observed for samples with higher Ni content. Increasing the Ni content was found to gradually lower the lithiation voltage, while delithiation voltage was not affected for x <= 0.25. As a result, Li15Si4 did not form during cycling for x > 0.15. The capacity trend of NixSi1-x alloys with composition suggested that the nanocrystalline NiSi2 phase had some activity toward Li, while the NiSi phase had no capacity toward Li. In situ XRD studies confirmed the activity of nanocrystalline NiSi2. The best cycling performance of NixSi1-x alloys was obtained for x = 0.20 with 94% capacity retention after 50 cycles. (C) The Author(s) 2015. Published by ECS.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据