In this study, (Al0.5CrFeNiTi0.25)N-x high-entropy films are prepared by a reactive direct current (DC) magnetron sputtering at different N-2 flow rates on silicon wafers. It is found that the structure of (Al0.5CrFeNiTi0.25)N-x high-entropy films is amorphous, with x = 0. It transforms from amorphous to a face-centered-cubic (FCC) structure with the increase of nitrogen content, while the bulk Al0.5CrFeNiTi0.25 counterpart prepared by casting features a body-centered-cubic (BCC) phase structure. The phase formation can be explained by the atomic size difference (). Lacking nitrogen, is approximately 6.4% for the five metal elements, which is relatively large and might form a BCC or ordered-BCC structure, while the metallic elements in this alloy system all have a trend to form nitrides like TiN, CrN, AlN, and FeN. Therefore, nitride components are becoming very similar in size and structure and solve each other easily, thus, an FCC (Al-Cr-Fe-Ni-Ti)N solid solution forms. The calculated value of is approximately 23% for this multicomponent nitride solid solution. The (Al0.5CrFeNiTi0.25)N-x films achieve a pronounced hardness and a Young's modulus of 21.45 GPa and 253.8 GPa, respectively, which is obviously much higher than that of the as-cast Al0.5CrFeNiTi0.25 bulk alloys.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据