期刊
JOURNAL OF POROUS MATERIALS
卷 23, 期 2, 页码 301-310出版社
SPRINGER
DOI: 10.1007/s10934-015-0082-y
关键词
Fe,Zn,Al-pillared montmorillonite; Catalyst wet peroxide oxidation; Orange II; Fe/Zn molar ratio; ZnFe2O4 nanoparticles
资金
- Innovative projects of Graduate students [YZZ13036]
Fe,Zn,Al-pillared montmorillonite (Mt) were prepared by ion exchange reaction. Effect of the Fe/Zn molar ratio in Fe,Zn,Al-pillaring solution on the structural properties of Fe,Zn,Al-Mt was examined. Characterization studies were performed by N-2-adsorption/desorption, ICP, FTIR, DR UV-Vis spectroscopy and XRD. The interlayer space, specific surface and volume of micropores of pillared-Mt was 18.8 a<<, 157 m(2) g(-1) and 0.114 cm(3) g(-1) respectively. Besides, the catalytic performance of Fe,Zn,Al-Mt was analyzed through wet peroxide oxidation of Orange II under mild experimental condition. The results indicated that the catalytic performance of Fe,Zn,Al-Mt was affected by the Fe/Zn molar ratio as following pattern: the obtained pillared solids with lower Fe/Zn molar ratios exhibited better catalytic performance and less iron leaching during the reaction. Moreover, the introduction of zinc into Mt shortened the induction time of reaction and improved the catalytic behaviour. Throughout this work, the chemical oxygen demand removal of OII was 77.1 % after the solution treated by Fe,Zn,Al(3/7)-Mt (defined as the Fe/Zn molar ratio of 3/7 in the pillaring solution) catalyst at temperature of 60 A degrees C and atmospheric pressure of 1 atm.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据