JOURNAL OF POLYMER SCIENCE PART A-POLYMER CHEMISTRY
卷 53, 期 13, 页码 1606-1616出版社
WILEY-BLACKWELL
DOI: 10.1002/pola.27602
关键词
alkyl-phosphonic acids; amphiphiles; coatings; colloidal polyaniline; conducting polymers; micelle; polyaniline; smart coatings
资金
- Agence Universitaire de la Francophonie (AUF)
Polyaniline (PANI) dispersions consisting of 270 to 380 nm sized particles were prepared by oxidation with ammonium peroxydisulfate (APS) in n-decylphosphonic acid (DPA) micellar solutions. The green dispersions do not undergo macroscopic precipitation for more than a year. The synthesized DPA doped PANI exhibited enhanced electrical conductivity (3.6 S cm(-1)) compared with DPA-PANI (2.3 x 10(-4) S cm(-1)) prepared by postsynthesis treatment of the PANI-base with DPA. It was shown that through protonation with decylphosphonic acid, polyaniline showed a significantly enhanced solubility in common organic solvents like chloroform, xylene, etc. The synthesized PANI was characterized by intrinsic viscosity, solubility, FT-IR, conductivity, SEM, and TGA measurements. The wide-angle X-ray diffraction study revealed the appearance of a peak located at low angles (d=29.4-35.3 angstrom) suggesting the formation of layered structure of PANI backbone separated by long alkyl side chains of DPA. The anticorrosive performance of the bilayer coatings composed of a bottom layer of DPA doped polyaniline covered with a polyvinyl butyral topcoat, have been demonstrated for steel exposed to neutral saline solutions. It was found that the inhibitive properties of DPA dopant provides further protection to the base metal through smart release when damage is produced on the surface of the coating. (c) 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2015, 53, 1606-1616
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据