DLC; pulsed discharge plasma CVD; band gap; photoconductivity; ESR
DLC films were deposited by a new pulsed DC discharge plasma chemical vapour deposition (CVD) using hydrogen and methane gas mixture. When methane concentration (Cm) i.e. CH(4)/(H(2) + CH(4)) was increased from 3 to 40%, the graphitization of the carbon film increases as evident from Raman study. When Cm was increased to 30%, DLC film shows photoconducting property. The white light photoconductivity (S=I(l)/I(d), where I(l) is light current and Id is dark current) measured with solar simulator under AM 1.5 condition was approximately 20 at room temperature. The photoconductivity was not clear when Cm was lower than 20%. ESR measurements also show that the electron spin density was slightly decreased with decreasing concentration of methane. Thus we can conclude here that at higher concentrations of methane at 30%, Sp(2) content of the film increases and the DLC film becomes photoconducting. (C) 2008 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据