A novel and simple method to synthesize SiO2-coated Fe nanocomposites with enhanced Cr (VI) removal under various experimental conditions

This study reported a facile one-step method for stabilizing iron nanoparticles (Fe NPs) with silica as a shell using borohydride reduction method combined with modified Stober method. The synthesized SiO2-coated Fe nanocomposites (Fe@SiO2) were used for reductive degradation of Cr (VI) through laboratory batch experiment. The monodispersed Fe NPs with a mean diameter of 25 nm were coated with a 10-20 nm thick SiO2 shell. The Cr (VI) removal tests demonstrated that the degradation ability of Fe@SiO2 was 83.64% higher than their uncoated counterparts. The Cr (VI) was converted to nontoxic Cr (III) with Fe@SiO2 and the rapid reduction of Cr (VI) followed a pseudo-first-order reaction kinetics. The removal rate constant increased from 0.006 to 0.231 min(-1) with increasing Fe NPs dose from 0.075 to 0.2 g.L-1. However, with an increase in initial Cr (VI) concentration, the reduction rate decreased. Despite the Cr (VI) reduction with Fe NPs was favorable under acid conditions, it was highly reduced by Fe@SiO2 until pH increased to 10. In addition, an increase in rate constant was achieved from 0.015 min(-1) at 15 degrees C to 0.076 min(-1) at 45 degrees C. Moreover, the interfering substances exerted various degrees of impact on Cr (VI) removal capacity. (C) 2012 Elsevier B.V. All rights reserved.