DESALINATION
卷 275, 期 1-3, 页码 133-140出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.desal.2011.02.045
关键词
Post-treatment; Heat-treatment; Stretching; Hollow fiber membrane; Polyurethane
资金
- National Natural Science Foundation of China [20874073]
- National 863 (high-tech research and development) Program of China [2007AA030304]
- Tianjin Science and Technology Key Support Plan [10SYSYJC27900]
Polyurethane-based (PU-based) hollow fiber membranes were fabricated by melt-spinning method and then treated under different conditions to investigate the effects of post-treatment on their morphology and performance. The post-treatment included two processes, a water bath post-treatment for 48 h at various temperatures and a dry air oven heat-treatment at 20 degrees C for 48 h. During the treatment process, membranes were treated at different draw ratios and their deformations were studied. Elastic deformation-recovery was associated with the treatment temperature and was affected slightly by draw ratio. For membranes treated in stress free conditions, pore size on the inner surface shrunk with increasing treatment temperature. Stretching could enlarge the mean and maximum pore size of membrane. The best water flux was obtained when the hollow fiber membranes were treated at 50 degrees C. and the least treatment duration was 50 min. Meanwhile, the extension ratio 3 was adopted as the optimal draw ratio. (C) 2011 Elsevier By. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据