期刊
CURRENT APPLIED PHYSICS
卷 13, 期 8, 页码 1769-1773出版社
ELSEVIER
DOI: 10.1016/j.cap.2013.06.005
关键词
ZnO nanowires; Response; Gas sensor; CO; Ethanol
资金
- Chonbuk National University
- National Research Foundation (NRF)
- Korea government (MEST) [NRF-2010-0019626, 2009-0093263, 20/2R/A2AA01006787]
- National Research Foundation of Korea [2009-0093263] Funding Source: Korea Institute of Science & Technology Information (KISTI), National Science & Technology Information Service (NTIS)
The ZnO NWs were applied as effective material for the fabrication of ethanol (C2H5OH) and carbon monoxide (CO) gas sensor. The ZnO NWs were grown by thermal evaporation techniques on non-catalytic Si (100) substrates. The average width and length of ZnO NWs was 60 nm and 20 mu m, respectively and they were single crystalline in nature. The maximum response was 51.64 at 300 degrees C for 1000 ppm of CO gas, while 104.23 at 400 degrees C for 250 ppm of ethanol gas. The response of ZnO NWs was very high for ethanol compared to the CO, whereas the recovery time for ethanol was very poor compare to CO gas. The response of ZnO NWs was about 25 times higher for ethanol compare to CO, at 400 degrees C for 100 ppm of each gas. The high response for ethanol is related to electron donating effect of ethanol (10e(-)) which was higher than the CO gas (2e(-)). The high response of ZnO NWs was attributed to large contacting surface area for electrons, oxygen, target gas molecule, and abundant channels for gas diffusion. (C) 2013 Elsevier B. V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据