CURRENT APPLIED PHYSICS
卷 10, 期 -, 页码 S278-S281出版社
ELSEVIER
DOI: 10.1016/j.cap.2009.11.061
关键词
Transparent conducting oxide; Al doped ZnO; Magnetron sputtering; Etching
Al doped ZnO (AZO) films were prepared by radio frequency (rf) magnetron sputtering with varying substrate temperature, working Ar gas pressure and rf power imposed on 2-inch ZnO-Al2O3 (2 wt%) target, and their electrical and structural properties together with the corresponding etching behavior in 0.5% HCl solution were examined The effect of rf power on the electrical and structural properties of AZO films was marginal, but in the case of working Ar gas pressure and substrate temperature, substantial variations in the electrical and structural properties were observed The optimum electrical properties were obtained for AZO film deposited at 150 C in lowest working pressure of 1 2 mTorr The behavior of crater formation upon etching varied significantly depending on the structure of the film, and it was shown that the etching rate could be expressed inversely proportional function of the crystallinity represented as (002) peak intensity Also, for films with similar crystallinity, ie (002) peak intensity, dense structured Film deposited at high temperature had much lower etching rate than open structured films deposited under high working Ar gas pressure (C) 2009 Elsevier B V All rights reserved
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据