CORROSION SCIENCE
卷 52, 期 7, 页码 2469-2480出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.corsci.2010.03.025
关键词
Steel reinforced concrete; SEM; Modelling studies; Interfaces; Rust
资金
- Engineering and Physical Sciences Research Council, UK
- National Natural Science Foundation of China [50538070, 50808157]
Reinforced concretes were corroded to varying degrees by exposing to cyclic NaCl spray and 40 degrees C drying. The amount of corrosion products and induced damage were measured using image analysis. We found that corrosion products can accumulate at steel-concrete interface as well as penetrate cement paste and deposit within hydration products, relicts of reacted slag, and air voids. As corrosion increases, the products tend to accumulate at the steel-concrete interface, while the amount penetrating cement paste remains relatively constant. Only a small amount of corrosion is needed to induce visible cover cracking. Implications on modelling time to cover cracking are discussed. (C) 2010 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据