CONSTRUCTION AND BUILDING MATERIALS
卷 51, 期 -, 页码 75-81出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.conbuildmat.2013.10.042
关键词
Steel reinforced concrete; Chloride; Pitting corrosion; Microcell; Macrocell
资金
- China Ministry of Science and Technology under National 973 project [2009CB623200]
Steel corrosion normally takes pitting pattern in chloride contaminated RC structures. This paper examines the localized corrosion rust accumulation process through electrochemical analysis. The coupled micro- and macro-cell corrosion process involved in typical chloride-induced corrosion is numerically simulated by employing the Finite Element Method (FEM). The modeling results show that macrocell corrosion rate may decrease drastically while microcell corrosion rate may not change so much during the gradual initiation process of corrosion around reinforcing steel. The non-uniform rust distribution around steel-concrete interface is found to be mainly caused by macrocell corrosion circulating between upper active and lower passive rebar surface. (C) 2013 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据