COMPOSITES SCIENCE AND TECHNOLOGY
卷 91, 期 -, 页码 50-54出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.compscitech.2013.11.026
关键词
Polymer-matrix composites (PMCs); Differential scanning calorimetry (DSC); Mechanical properties; Scanning electron microscopy (SEM)
资金
- Basic Research Fund of Beijing Institute of Technology [3100012211304]
High performance recyclable polyethylene naphthalate (PEN) single-polymer-composites (SPCs) were successfully produced by using the undercooling melt film stacking method within 220-260 degrees C. A significant large processing temperature window (48 degrees C) was determined by differential scanning calorimetry. The tensile properties of the PEN SPCs as a function of compaction temperature and holding time were studied. As the compaction temperature increased, the tensile strength increased first and then decreased. Similar trend was observed as the holding time increased. In order to obtain the best tensile property, a longer holding time is needed when the compaction temperature is lower. A tensile strength of 224 MPa and a tensile modulus of 8.4 GPa were achieved at an optimum processing condition, compaction temperature of 240 degrees C and holding time of 10 mm. The tensile strength of the PEN SPCs was 3.6 times higher than that of the non-reinforced PEN. Scanning electron microscopy showed good interfacial adhesion between fibres and matrix. (C) 2013 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据