期刊
COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING
卷 59, 期 -, 页码 1-8出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.compositesa.2013.12.009
关键词
Mechanical testing; Compression molding; Preform; Thermoplastic resin
From the actual usage of natural fiber reinforced composites, textile composites are desired. In the present study, hemp fiber reinforced poly(lactic acid) composites were molded with micro-braiding technique. At first micro-braided yarn (MBY) was fabricated. Then, plain woven fabrics were weaved on a loom. In order to optimize molding condition, three molding conditions were selected based on the previous study on unidirectional composites. Tensile and shear tests were conducted on the specimens. Tensile and shear strength is highest for molding temperature 190 degrees C, molding pressure 1 MPa and molding time 4 min. Higher molding pressure induce pouring out of matrix from the mold die, which result in lack of matrix. At higher temperature, slight decomposition of hemp fiber also occurred. Cross-ply laminates and weft knitted composites were also molded for comparison. Tensile properties of textile composites were much lower than cross-ply laminates, because of undulation structures. (C) 2013 Published by Elsevier Ltd.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据