Study on the oxidation resistance and tribological behavior of glass lubricants used in hot extrusion of commercial purity titanium

Glass lubricants have great potential in industrial metal forming processes such as hot extrusion of titanium and titanium alloys. In this work, based on the extrusion process of commercial-purity titanium (TA2) at 800 degrees C, glass lubricants with low melting points are designed. The thermal properties, high-temperature oxidation resistance and friction properties of uncoated and glass-coated TA2 samples are systemically studied, which reveals the good lubricating and anti-oxidation properties of the samples. The glass lubricant melts into a viscoelastic film at 800 degrees C to insulate TA2 from oxygen and reduce friction, and automatically peel off during cooling due to the significantly mismatched thermal expansion between the glass coating and TA2 substrate. This work provides a guidance for designing glass-based lubricants used in hot extrusion of metals.