卷 40, 期 8, 页码 13371-13379出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2014.05.053
关键词
CRT glass; Recycling; Glass foams; Egg shells
资金
- CICECO [PEst-C/CTM/LA0011/2013]
- FCT, Portugal [SFRH/BPD/86275/2012]
- Fundação para a Ciência e a Tecnologia [SFRH/BPD/86275/2012] Funding Source: FCT
Panel (P) and funnel (F) glasses from Cathode Ray Tube (CRT) have been used to obtain glass foams by a simple and economic processing route, consisting of direct heating the glass powders at relatively low temperatures (650-750 degrees C) using different foaming agents (FA) such as egg shells, calcite, dolomite. Mixtures in different proportions of P and F glass powders were tested and the effects of composition and heat treatment temperature on the foaming behaviour were evaluated. Glass foams featuring apparent density and compressive strength values of 0.29 g/cm(3) and 2.34 MPa, respectively, could be produced from a P/F ratio = 1 with added 3 wt% of egg shells upon heat treating at 700 degrees C for 15 min. The P/F ratio was found to strongly influence the foaming behaviour and, consequently, the physical properties of the final foam glass. The relative performance of other foaming agents under a given set of experimental conditions revealed to be dependent on the type of glass (composition and thermal properties). (C) 2014 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据