CERAMICS INTERNATIONAL
卷 40, 期 7, 页码 10329-10335出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2014.03.005
关键词
Fiber; Porous ceramics; Reinforcing; YSZ
资金
- National Natural Science Foundation of China (NSFC) [51172119]
Porous YSZ ceramics were prepared by a gel-casting method using tert-butyl alcohol (TBA) as solvent and Al2O3 fiber as reinforcement. Effects of sintering temperature, soaking time and Al2O3 fiber content on porosity, microstructure, compressive strength, and fracture toughness of the porous ceramics were studied. Compressive strength of porous YSZ ceramics was improved while the porosity decreased with the increase of sintering temperature and soaking time. Addition of Al2O3 fibers significantly strengthened and toughened porous YSZ ceramics; however, the laws of strengthening and toughening were different. The strength of the porous YSZ ceramics reached maximum at the addition of 10 vol% Al2O3 fibers, and the corresponding compressive strength and flexural strength were 100.2 +/- 25.4 MPa and 61.5 +/- 11.3 MPa, respectively. Fracture toughness of the porous YSZ ceramics monotonically increased with increasing of Al2O3 fibers, and could be improved from 0.5 MPa m(1/2) MPa m(1/2) (improved by 140%). The strengthening and toughening mechanisms of Al2O3 fibers were discussed. (C) 2014 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据