CERAMICS INTERNATIONAL
卷 39, 期 5, 页码 5137-5143出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2012.12.009
关键词
Magnetic nanomaterials; Coercivity; Superparamagnetism; Polyaniline
资金
- Fatih University under BAP [P50021104-B]
Polyaniline (PANI)/Cobalt-manganese ferrite, (PANI)/Co0.5Mn0.5Fe2O4, nanocomposite was synthesized by oxidative chemical polymerization of aniline in the presence of ammonium peroxydisulfate (APS). Microwave assisted synthesis method was used for the fabrication of core CoFe2O4 nanoparticles. The structural, morphological, thermal and magnetic properties of the nanocomposite were investigated in detail by X-ray diffraction (XRD), fourier-transform infrared spectroscopy (FT-IR), thermogravimetric analysis (TGA), scanning electron microscopy (SEM) and vibrating sample magnetometer (VSM). The average crystallite size of (PANI)/Co0.5Mn0.5Fe2O4 nanocomposite by the line profile method was 20 +/- 9 nm. The magnetization measurements revealed that (PANI)/Co0.5Mn0.5Fe2O4 nanocomposite has superparamagnetic behavior with blocking temperature higher than 300 K. The saturation magnetization of the composite is considerably low compared to that of CoFe2O4 nanoparticles due to the partial replacement of Co2+ ions and surface spin disorder. As temperature decreases, both coercivity and strength of antiferromagnetic interactions increase which results in unsaturated magnetization of the nanocomposite. (C) 2012 Elsevier Ltd and Teama Group S.r.l. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据