CERAMICS INTERNATIONAL
卷 34, 期 4, 页码 709-713出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2007.09.041
关键词
dielectric properties; ferroelectric properties; perovskites; ball milling
Pb0.99Nb0.02[(Zr0.60Sn0.40)(0.94)Ti-0.06](0.98)O-3 powders were synthesized from oxide mixtures of Pb3O4, Nb2O5, ZrO2, SnO2, and TiO2 using a Fritsch P4 (TM) vario-planetary ball milling system. The perovskite structure of PNZST powder can be obtained well after 14 h milling and crystallite size of the powders greatly reduced to 20-30 nm. The resultant powders have better sinterability characteristics to obtain dense ceramic bodies at low temperature. The dielectric constant of samples shows a maximum at 1150 degrees C and the PEMC to PESC transformation temperature shifts to higher temperature with an increase in grain size. The field-induced strain reaches maximum longitudinal strain of 0.32% and the P-E hysteresis loop shows much higher squareness at 1150 and 1200 degrees C. The measured dielectric and antiferroelectric properties of the PNZST ceramics were found to be comparable to those from other processing techniques. (C) 2007 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据