CERAMICS INTERNATIONAL
卷 34, 期 2, 页码 253-255出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2006.08.018
关键词
porous SiC ceramics; silicone resin; preceramic polymer pyrolysis; porosity; fracture strength
Commercially available silicone resin and silicon carbide (SiC) powders were adopted as the starting materials for the fabrication of porous SiC ceramics. During the heat treatment process, silicone resin experienced an organic-inorganic transformation and acted as the bonding material between SiC particles at a low temperature of 1000 degrees C. The mean particle size of starting SiC powders and silicone resin content can control the pore size, open porosity and fracture strength. The flexural strength of porous SiC ceramics increases with increasing silicone resin content and decreasing mean particle size of SiC powders. Larger pores can be obtained with coarser starting SiC powders and higher silicone resin content. The fracture surface of porous SiC ceramics was observed. (c) 2006 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据