CARBON
卷 49, 期 9, 页码 2893-2904出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.carbon.2011.02.063
关键词
-
资金
- Department of Education and Learning NI (DEL)
- QUB
- Royal Academy of Engineering, Leverhulme
Multi-walled carbon nanotube (MWCNT)/polymethyl methacrylate (PMMA) composites with loadings ranging from 0.1 to 1.0 wt.% were prepared for use as bone cement. Unfunctionalised, carboxyl and amine functionalised MWCNT were used. Thermal properties were characterised in accordance with the International Standard for acrylic cements, ISO 5833:2002. The rate of reaction exotherm generated and thermal necrosis index (TNI) values were calculated. Polymerisation kinetics were characterised using parallel plate rheology and the exotherm during polymerisation was reduced by approximate to 4-34%, as a consequence of the MWCNT thermal conductivity. The rate of reaction was significantly altered, such that the setting times of the cements were extended (approximate to 3-24%). Consequently, significant decreases in TNI values (ranging from 3% to 99%) were recorded, which could reduce the exothermic temperatures experienced in vivo and therefore prevent the likelihood of polymerising PMMA cement causing thermally-induced bone tissue necrosis. Thermal data was supported by the rheological characterisation results. Onset of polymerisation for PMMA cement exhibited a strong linear increase as a function of MWCNT loading, however, polymer gelation was not affected to the same degree. It is proposed that the chemically functionalised MWCNT altered PMMA bone cement polymerisation kinetics, reducing the rate of polymerisation, and hence, the reaction exotherm. Crown Copyright (C) 2011 Published by Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据