期刊
JOURNAL OF ALLOYS AND COMPOUNDS
卷 634, 期 -, 页码 32-36出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2015.02.021
关键词
Transition metal chalcogenides; Layered compounds; Thermoelectric; Titanium chalcogenide
资金
- IdsFundmat project through an Erasmus Mundus fellowship
Polycrystalline samples of copper intercalated CuxTiS1.5Se0.5 (x = 0, 0.025, 0.05 and 0.1) are synthesized by classical high temperature reaction. The resulting powders are successfully densified by using spark plasma sintering. As expected, XRD refinements show that Cu intercalation between TiS1.5Se0.5 slabs induces an increase in the c lattice parameter. Electrical resistivity and Seebeck coefficient decrease drastically with increasing Cu content, direct consequence of the increased carrier concentration. In parallel, the lattice thermal conductivity of CuxTiS1.5Se0.5 is significantly reduced compared to unfilled TiS1.5Se0.5. Overall, the dimensionless thermoelectric figure of merit increases with temperature and reaches a maximum value of 0.54 at 700 K for Cu0.05TiS1.5Se0.5, the highest value so far observed in layered titanium chalcogenides. (C) 2015 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据