Polymers; Plastics; Composite materials; Mechanical properties; X-ray diffraction; Liquid crystals
资金
- UGC, New Delhi, India
Nanocomposites of polyether imide (PEI) and liquid crystalline polymer (LCP) with either MWCNT, Expanded Graphite (EG) or in combination of both EG and PEI-co-Silicon Rubber were prepared by melt blending process. The compatibility between the polymeric phases (PEI&LCP) was observed to be increased by the addition of PEI-co-Silicon Rubber while the only MWCNT added system (PLC) resulted in smaller LCP droplets. A continuous morphology was produced in presence of both PEI-co-Silicon Rubber and EG both added system (PLGR). This was due to the compatibilizing effect of PEI-co-Silicon Rubber. FTIR analysis revealed interaction between PEI and LCP in presence of PEI-co-Silicon Rubber. Remarkable increment of storage modulus was observed with the addition of EG and PEI-co-Silicon Rubber. Transmission Electron Microscope (TEM) analysis showed better dispersion of multiple graphene layers of EG in presence of PEI-co-Silicon Rubber compatibilized system. Tensile and Young's modulus both were highest for EG/ PEI-co-Silicon Rubber added system. This is due to flexible compatibilizing effect of PEI-co-Silicon Rubber which delayed the detachment of LCP domain from the PEI matrix and thus detains the fracture. (C) 2014 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据