JOURNAL OF ALLOYS AND COMPOUNDS
卷 624, 期 -, 页码 116-125出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2014.10.177
关键词
Mg-Y-Zn-Zr alloys; Indirect extrusion; Microstructures; Mechanical properties; Corrosion behaviors
资金
- National Basic Research Program of China [2013CB632203]
- National Key Technology R&D Program of China [2012BAF09B01]
- Liaoning Provincial Natural Science Foundation of China [201202072, 2014028027]
- Program for Liaoning Excellent Talents in University [LJQ2012023]
- Fundamental Research Foundation of Central Universities [N120509002, N120309003]
Three Mg-Y-Zn-Zr alloys have been designed with specific Y/Zn mole ratios around 1.32 for the purpose of high performance. Microstructures, mechanical properties and corrosion behaviors of the alloys have been studied. A wide distribution of compact and thick X-phase could promote the mechanical properties and corrosion resistance drastically. Moreover, a solidification behavior was proposed to understand the alternant distribution of X-phase (Mg12YZn) and W-phase (MgY2Zn3). After hot extrusion, the corrosion resistance and mechanical properties of the alloys are strongly improved, due to the grain refinement and dispersive distribution of X-phase. Among the designed alloys, a high performance MgY3.8Zn3Zr0.18 alloy was prepared by conventional casting and subsequent hot extrusion process. It owns an ultimate and yield strength of 420 MPa and 300 MPa, respectively, as well as the best corrosion resistance. (C) 2014 Elsevier B.V. All rights reserved.