Ultrasonic surface rolling processing; 40Cr; Microstructure; Nano-structured layer; Mechanical properties
类别
资金
- National Science Foundation [50405019]
Ultrasonic surface rolling processing (USRP) was applied on quenched and tempered 40Cr. Microstructure observations of USRP specimen surface indicate that the processing can both get nano-structured layers, with grain size of 3-7 nm, and reduce the surface roughness to 0.05 mu m. Life of the rolling processing tip is about 800 times longer than the. fixed one, which makes the processing practical and economical. Tests of mechanical properties show that microhardness of USRP specimen surface was increased by 52.6%; residual compressive stress can reach -846 MPa. It has been determined by contrast wear test that USRP can reduce friction coefficient and improve the wear-resistant property. (C) 2008 Elsevier B. V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据