期刊
APPLIED PHYSICS LETTERS
卷 100, 期 16, 页码 -出版社
AMER INST PHYSICS
DOI: 10.1063/1.4704926
关键词
annealing; high-pressure effects; indium compounds; thin film transistors; vacancies (crystal)
资金
- MKE/KEIT [10025225]
- [10035225]
This study examined the effect of oxygen (O-2) high pressure annealing (HPA) on tin-doped indium oxide (ITO) thin film transistors (TFTs). The HPA-treated TFT at 150 degrees C exhibited a high saturation mobility (mu(SAT)), low subthreshold gate swing (SS), threshold voltage, and I-on/off of 25.8 cm(2)/Vs, 0.14 V/decade, 0.6 V, and 2 x 10(8), respectively. In contrast, the ambient-annealed device suffered from a lower mu(SAT) and high SS value of 5.2 cm(2)/Vs and 0.58 V/decade, respectively. This improvement can be attributed to the decreased concentration of oxygen vacancy defects in the ITO channel layer during the effective O-2 HPA treatment, which also resulted in smaller hysteresis and less degradation of the drain current under positive bias stress conditions. (C) 2012 American Institute of Physics. [http://dx.doi.org/10.1063/1.4704926]
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据