Effect of Silane Coupling Agents on Rice Straw Fiber/Polymer Composites

The effect of coupling agents and electron beam (EB) irradiation dose on the mechanical properties of composites made from rice straw fibers and polymers have been studied. Samples were made by hot pressing of mix composition at 130A degrees C. The pressed samples were subjected to electron beam irradiation dose ranged from 10 to 50 kGy. Increasing the electron beam irradiation dose increased the value of flexural strength, modulus of elasticity and impact strength. It was also observed that, the properties of composites containing gamma-aminopropyltrimethoxy silane (A-1100) are lower than those of composites containing N-(2aminoethyl)-3-amino propyltrimethoxy silane (A-700) coupling agents. These are attributed to a hydrogen bonding formation between the amine or protonated amine and the hydroxyl groups of rice straw fibers. The presence of coupling agents in the composites during the EB irradiation process produce a more free radicals which are enough to form a chemical bonding between the rice straw fiber and polymer. The thickness swelling and water absorption values decrease with increasing the EB irradiation dose with presence of coupling agents in the composite.