ADVANCED POWDER TECHNOLOGY
卷 24, 期 6, 页码 913-920出版社
ELSEVIER
DOI: 10.1016/j.apt.2013.01.003
关键词
Mo5SiB2; Sparking plasma sintering; Sintering temperature; Heating rate; Composition
资金
- National Natural Science Foundation of China [50871012]
- National Key Basic Research Program of China [2011CB605502]
Mo5SiB2 (T2) was synthesized by sparking plasma sintering (SPS) under different heating rates and sintering temperatures. The powder mixture with a T2 composition (Mo-12.5Si-25B (at.%)) failed to produce the T2 single-phase alloy due to the volatilization of Si during SPS process. Extra 0.5 at.% Si added to this mixture offset the volatilization loss. It has been found that heating of the mixture at low heating rates favored the formation of binary phases in the solid state at medium temperatures. In this work, the T2 alloy with a fine-grained microstructure was obtained via a liquid-solid reaction when the mixture was heated fleetly to the temperatures above the silicon melting point at the rapid heating rate of 200 degrees C/min. The sintering temperature at 1500 degrees C for T2 synthesis is beneficial to enhance further densification, as well as to avoid abnormal grain growth at higher temperatures. (C) 2013 The Society of Powder Technology Japan. Published by Elsevier B. V. and The Society of Powder Technology Japan. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据