Quenching and partitioning; Bainite; Retained austenite; Ductility; Toughness
资金
- National Natural Science Foundation of China [51301012]
Three heat-treatment routes incorporating bainite formation, namely bainite-based quenching plus tempering, bainite austempering and bainite-based quenching plus partitioning (BQ&P), were applied to a medium-carbon Mn-Si-Cr alloyed steel. An optimum combination of strength, ductility and toughness was achieved after the BQ&P treatment (ultimate tensile strength: 1688 MPa; total elongation: 25.2%; U-notch impact toughness at -40 degrees C: 48 J cm(-2)). The enhanced mechanical properties were attributed to an increased amount of refined filmy retained austenite (22 vol.%, nanometer width range: <100 nm and submicron width range: 100-500 nm). The formation process of the bainitic microstructure as well as martensite and retained austenite was revealed by conducting dilatometry, X-ray diffraction, scanning electron microscopy, electron backscatter diffraction and transmission electron microscopy (TEM). The effect of the retained austenite on mechanical properties was discussed in terms of its size and morphology. (C) 2014 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据