期刊
ACS APPLIED MATERIALS & INTERFACES
卷 6, 期 17, 页码 15448-15455出版社
AMER CHEMICAL SOC
DOI: 10.1021/am504057y
关键词
nanowires; quantum dots; solar cells; interface; counter electrods
资金
- National Key Project on Basic Research [2011CB808700, 2012CB932900]
- National Natural Science Foundation of China [91127044, 21173237, 21121063]
- Chinese Academy of Sciences
Among the issues that restrict the power conversion efficiency (PCE) of quantum-dot-sensitized solar cells (QDSSCs), insufficient catalytic activity and stability of counter electrodes (CEs) are critical but challenging ones. The state-of-the-art Cu/Cu2S CEs still suffer from mechanical instability and uncertainty due to the reaction of copper and electrolyte. Herein, ITO@Cu2S core-shell nanowire arrays were developed to fabricate CEs for QDSSCs, which have no such issues in Cu/Cu2S CEs. These nanowire arrays exhibited small charge transfer resistance and sheet resistance, and provided more active catalytic sites and easy accessibility for electrolyte due to the three-dimensional structure upon use as CEs. More interestingly, it was found that the interface of ITO/Cu2S significantly affected the performance of ITO@Cu2S nanowire array CEs. By varying synthetic methods, a series of ITO@Cu2S nanowire arrays were prepared to investigate the influence of ITO/Cu2S interface on their performance. The results showed that ITO@Cu2S nanowire array CEs with a continuous Cu2S nanocrystal shell fabricated via an improved cation exchange route exhibited excellent and thickness-dependent performance. The PCE of corresponding QDSSCs increased by 11.6 and 16.5% compared to that with the discrete Cu2S nanocrystal and the classic Cu/Cu2S CE, respectively, indicating its promising potential as a new type of CE for QDSSCs.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据