卷 8, 期 5, 页码 -出版社
MDPI
DOI: 10.3390/met8050342
关键词
selective laser melting; NiTi; shape memory; pseudoelasticity
资金
- Ministry of Science and Technology, Taiwan, R.O.C [105-2221-E-151 -021 -MY2]
In this study, an optimal selective laser melting (SLM) process for manufacturing dense NiTi alloy with pseudoelasticity and shape-memory capability was proposed. The microstructure, phase-transformation temperature, shape memory capability, and pseudoelasticity were investigated by scanning electron microscopy, X-ray diffraction, differential scanning calorimetry, and bending and tensile tests. NiTi powder with a particle size > 45 mu m was selected for the subsequent SLM process, because it exhibited a Ni/Ti ratio of similar to 1 and a lower oxygen content than powders with smaller particle sizes. A thin-walled disk (0.48 mm thick) and cuboid samples (5 mm thick) were prepared for investigating the variation in the homogeneity of the microstructure. The thin-walled SLM-NiTi sample exhibited a marginally inhomogeneous microstructure between layers, and defects existed in the previously formed side. The cuboid SLM-NiTi sample was fabricated without undesirable secondary phases, and it exhibited a 100% shape-recovery rate under 2% bending strain and completely pseudoelastic under 3% strain. Also, the SLM-NiTi exhibited lower phase-transformation temperatures and a broader phase-transformation range than the original NiTi. The phase-transformation range can be reduced by annealing.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据