期刊
METALS
卷 8, 期 2, 页码 -出版社
MDPI
DOI: 10.3390/met8020088
关键词
serrated flow; PLC effect; dynamic strain aging; particle reinforcement; acoustic emission; jump tests; aluminum alloy
资金
- German Research Foundation (Deutsche Forschungsgemeinschaft, DFG) through the Collaborative Research Center [SFB 692]
The Portevin-Le Chatelier (PLC) effect often results in serrated plastic flow during tensile testing of aluminum alloys. Its magnitude and characteristics are often sensitive to a material's heat treatment condition and to the applied strain rate and deformation temperature. In this study, we analyze the plastic deformation behavior of an age-hardenable Al-Cu alloy (AA2017) and of a particle reinforced AA2017 alloy (10 vol. % SiC) in two different conditions: solid solution annealed (W) and naturally aged (T4). For the W-condition of both materials, pronounced serrated flow is observed, while both T4-conditions do not show distinct serrations. It is also found that a reduction of the testing temperature (-60 degrees C, -196 degrees C) shifts the onset of serrations to larger plastic strains and additionally reduces their amplitude. Furthermore, compressive jump tests (with alternating strain rates) at room temperature confirm a negative strain rate sensitivity for the W-condition. The occurring PLC effect, as well as the propagation of the corresponding PLC bands in the W-condition, is finally characterized by digital image correlation (DIC) and by acoustic emission measurements during tensile testing. The formation of PLC bands in the reinforced material is accompanied by distinct stress drops as well as by perceptible acoustic emission, and the experimental results clearly show that only type A PLC bands occur during testing at room temperature (RT).
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据