Hierarchically porous niobium phosphate (NbP) was synthesised via a sol-gel method accompanied by phase separation and employed as a catalyst for fructose dehydration. The niobium precursor was prepared by digesting ammonium niobate(v) oxalate in aqueous H2O2 with citric acid as a chelating agent to prevent the precipitation of niobium hydroxide. Poly(acrylamide) and poly(ethylene glycol) were used as phase separation inducers to produce co-continuous macropores and gel skeletons. The NbP sample calcined at 600 degrees C for 8 h had a high surface area (S-BET approximate to 140 m(2) g(-1)) and large acidity (0.84 mmol-NH3 g(-1)). The NbP monolith was amorphous after calcination at 600 degrees C and transformed into an -NbOPO4 phase at 1000 degrees C. The NbP monolith calcined at 600 degrees C was an efficient acid catalyst for the dehydration of fructose to 5-hydroxymethylfurfural in water (70% yield) or in aqueous dimethyl sulfoxide (90% yield). The productivity of HMF reached 7.3 x 10(-2) mol h(-1) per kg-solution at an initial fructose concentration of 10.0 wt% in water with a catalyst loading of 2.0 wt%.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据