Hydrogen trapping in T24 Cr-Mo-V steel weld joints—microstructure effect vs. experimental influence on activation energy for diffusion
出版年份 2018 全文链接
标题
Hydrogen trapping in T24 Cr-Mo-V steel weld joints—microstructure effect vs. experimental influence on activation energy for diffusion
作者
关键词
Creep-resisting materials, Diffusion, Experiment design, Hydrogen embrittlement, Weld metal
出版物
Welding in the World
Volume 62, Issue 2, Pages 277-287
出版商
Springer Nature
发表日期
2018-01-08
DOI
10.1007/s40194-017-0546-6
参考文献
相关参考文献
注意：仅列出部分参考文献，下载原文获取全部文献信息。- Influence of welding parameters on diffusible hydrogen content in high-strength steel welds using modified spray arc process
- (2017) Thomas Schaupp et al. Welding in the World
- Thermal desorption analysis for hydrogen trapping in microalloyed high-strength steels
- (2017) Enrico Steppan et al. Welding in the World
- Effect of hydrogen on mechanical properties of heat affected zone of a reactor pressure vessel steel grade
- (2016) Michael Rhode et al. Welding in the World
- Hydrogen degradation effects on mechanical properties in T24 weld microstructures
- (2016) Michael Rhode et al. Welding in the World
- The effect of nanosized (Ti,Mo)C precipitates on hydrogen embrittlement of tempered lath martensitic steel
- (2014) Akihide Nagao et al. ACTA MATERIALIA
- Three-dimensional imaging of hydrogen blister in iron with neutron tomography
- (2014) Axel Griesche et al. ACTA MATERIALIA
- Hydrogen determination in 22MnB5 steel grade by use of carrier gas hot extraction technique
- (2014) S. Salmi et al. Welding in the World
- Modeling of Combined Anodic Dissolution/Hydrogen-Assisted Stress Corrosion Cracking of Low-Alloyed Power Plant Steels in High-Temperature Water Environments
- (2013) Hans Hoffmeister et al. CORROSION
- Hydrogen trapping in high strength martensitic steel after austenitized at different temperatures
- (2013) Yan Liu et al. INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
- Computational analysis of geometrical factors affecting experimental data extracted from hydrogen permeation tests: III – Comparison with experimental results from the literature
- (2013) E. Legrand et al. INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
- Influence of Dehydrogenation Heat Treatment on Hydrogen Distribution in Multi-Layer Welds Of Cr-Mo-V Steel
- (2013) Masamitsu Abe et al. Welding in the World
- Heat treatment Effects on The Reduction of Hydrogen in Multi-Layer High-Strength Weld Joints
- (2013) Tobias Mente et al. Welding in the World
- Evaluation of hydrogen trapping in high strength steels by thermal desorption spectroscopy
- (2012) D. Pérez Escobar et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Internal and surface damage of multiphase steels and pure iron after electrochemical hydrogen charging
- (2011) D. Pérez Escobar et al. CORROSION SCIENCE
- Thermal Desorption Analysis of Hydrogen in High Strength Martensitic Steels
- (2011) M. Enomoto et al. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE
- Hydrogen trapping in martensitic steel investigated using electrochemical permeation and thermal desorption spectroscopy
- (2011) S. Frappart et al. SCRIPTA MATERIALIA
- The influence of hydrogen charging on the notch tensile properties and fracture behaviour of dissimilar weld joints of advanced Cr–Mo–V and Cr–Ni–Mo creep-resistant steels
- (2010) J. Blach et al. ENGINEERING FAILURE ANALYSIS
Find Funding. Review Successful Grants.
Explore over 25,000 new funding opportunities and over 6,000,000 successful grants.
ExploreCreate your own webinar
Interested in hosting your own webinar? Check the schedule and propose your idea to the Peeref Content Team.
Create Now