卷 35, 期 6, 页码 542-549出版社
TAYLOR & FRANCIS LTD
DOI: 10.1080/02670844.2018.1433774
关键词
Superhydrophobic; fouling; corrosion; coating
资金
- National High-Tech Research & Development Program of China [2012AA053001]
A preparation technology of superhydrophobic coating on copper substrate was studied. Surface morphology and wettability of the superhydrophobic coating were characterised. The preparation mechanism was analysed. Corrosion and fouling behaviours of the superhydrophobic coating were investigated by electrochemical workstation and immersion experiments. The results show that ultrasonic assistance can shorten etching time and improve the etching uniformity of copper substrate. The optimum fabrication process parameters of superhydrophobic coating on copper substrate were obtained. The concentration of octadecanoic acid in the ethanol solution is 0.02 mol L-1, the immersion temperature is 35 degrees C and the immersion time is 120 h. Under these conditions, micro-nano long-strip structure can be formed on the surface of copper substrate, and the static contact angle can be up to 157 degrees and contact angle hysteresis is 4.2 degrees. The superhydrophobic coating shows better anti-corrosion and anti-fouling properties on copper substrate compared with the surface of bare copper.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据