MATERIALS CHEMISTRY AND PHYSICS
卷 210, 期 -, 页码 111-119出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.matchemphys.2017.09.057
关键词
High-entropy alloy; Cellular precipitate; Tensile test
资金
- Ministry of Science and Technology, Taiwan (R.O.C.) [106-2218-E-007-019, 106-2923-E-007-002-MY2]
In this work, a precipitation strengthened high entropy alloy was subjected to thermo-mechanical process in order to homogenize the grain microstructure. Tensile tests from room temperature to 1000 degrees C were conducted; microstructures were observed by scanning electron microscope and transmission electron microscope. Formation of cellular precipitate along grain boundaries was observed and could be related to hot tensile ductility drop at 750 degrees C (1023 K). Experimental analysis has indicated that driving force for the formation of cellular precipitates could be resulted from the chemical instability of supersaturation after annealing and migration of grain boundaries, and this phenomenon could be suppressed either through alloy design to increase gamma-prime solvus, and to hinder the migration of grain boundaries. This study serves as a guideline to design composition and thermo-mechanical process for precipitation strengthened high entropy alloys. (C) 2017 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据