Effects of microstructure transformation on mechanical properties, corrosion behaviors of Mg-Zn-Mn-Ca alloys in simulated body fluid

Magnesium and its alloys have unique advantages to act as resorbable bone fixation materials, due to their moderate mechanical properties and biocompatibility which are similar to those of human tissue, However, early resorption and insufficient mechanical strength are the main problems that hinder their application. Herein, the effects of microstructure transformation on the mechanical properties and corrosion performance of Mg-Zn-Mn-Ca were investigated with electrochemical and immersion measurements at 37 degrees C in a simulated body fluid (SBF), The results showed that the number density of Ca2Mg6Zn3/Mg2Ca precipitates was remarkably reduced and grain sizes were gradually increased as the temperature increased. The alloy that received the 420 degrees C/24 h treatment demonstrated the best mechanical properties and lowest corrosion rate (5,94 mm/a) as well as presented a compact and denser film than the others. The improvement in mechanical properties could be explained by the eutectic compounds and phases (Mg2Ca/Ca2Mg6Zn3) gradually dissolving into a matrix, which caused severely lattice distortion and facilitated structural re arrangement of the increased Ca solute, Moreover, the difference in potential between the precipitates and the matrix is the main essence for micro galvanic corrosion formation as well as accelerated the dissolution activity and current exchange density at the Mg/electrolyte interface. As a result, the best Mg alloys corrosion resistance must be matched with a moderate grain size and phase volume fractions.